Metal powder (pure copper), water and non-toxic binding materials.
• Shrinkage: 20%
• Firing Temp.:
Ramp at full speed to 1,700°F–1,800°F (927°C–982°C) and hold for 3 hours (total
firing time, including ramp-time, will be about 4 hours). Most firings perform
well at 1,700°F; however, if you discover that your pieces are not sintering
properly, try firing them at 1,800°F. If blistering occurs at 1,800°F, slightly
decrease the firing temperature. If you plan to enamel the piece, please follow
the recommended firing schedule listed in the included instructions.
Just as PMC® does, COPPRclay™ metal clay
provides an incredible artistic range. And, because it is copper, it is also so
economical that you can use it for large pieces--even sculptures--very
affordably! Like its precious-metal counterparts, COPPRclay can be pinched,
rolled, sculpted, cut or manipulated any way you like. Then fire it, and the
binder burns away, leaving a solid, pure copper object. Create jewelry, jewelry
components, or custom-crafted specialized tools. You can even practice new
techniques or design ideas using COPPRclay, then apply your new skills to
precious metals. And because COPPRclay is pure copper, it’s great for artists
who enjoy applying enamels (make sure to follow the recommended firing schedule
included with your COPPRclay and listed on copprclay.com).